Applicable for two-component systems, including waterborne plastic coatings, waterborne metal coatings, waterborne wood coatings, and two-component topcoat clear coatings
Chat Now Download TDSDescription
L-9203W is a hydroxyl-containing acrylic resin dispersion modified by a special process. The paint film has the characteristics of high hardness, high gloss and high fullness. L-9203W can be mixed with water-based isocyanate curing agent to prepare two-component industrial paint and automotive repair paint, or mixed with amino resin to prepare high-temperature baking paint. The obtained paint film has high gloss, high hardness, excellent chemical resistance, water resistance, solvent resistance, weather resistance and stain resistance. L-9203W also demonstrates very good leveling and flow properties. Compared with L-9201W, L-9203W offers a cost advantage.
Technical Data
| Appearance | Milky white emulsion |
|---|---|
| Viscosity(mPa.s) | 800-3,000 |
| Solid content % | 45±2 |
| Hydroxyl content | 3.8 |
| pH value | 7.5±0.5 |
| Average particle size (nm) | 80-120 |
Product Features
It has strong versatility, high cost performance, high bearing capacity for pigments and fillers, and good adhesion to ABS, ABS/PC, PC, wood equipment, and metal. Excellent flexibility, water resistance, scrub resistance and alkali resistance, high gloss, high hardness, high fullness and high weather resistance.
Applications
Applicable for two-component systems, including waterborne plastic coatings, waterborne metal coatings, waterborne wood coatings, and two-component topcoat clear coatings
Reference Formula
| Main Component | Curing Agent | ||
|---|---|---|---|
| Water | 10.8 | Water-based Curing Agent | 80 |
| Film-forming Additives | 3.5 | PMA | 20 |
| Anti-mildew Fungicides | 0.2 | Total | 100 |
| L-9203W Water-based Resin | 70 | ||
| Lencolo 1190W Dispersant | 0.2 | ||
| Lencolo 2024W Defoaming Agent | 0.2 | ||
| Lencolo 3245W Substrate Wetting Agent | 0.3 | ||
| Lencolo 3103 Soft Touch Leveling Agent | 0.3 | ||
| Color Paste | 14 | ||
| Thickening Agent | 0.3 | ||
| PH Value Adjuster | 0.2 | ||
| Total | 100 |
Main Component : curing Agent = 4~5 : 1
Precautions
The product should be stored in a tightly sealed container, protected from freezing and excessive heat. The recommended storage temperature is 10 – 25 °C.
Storage Conditions
To prevent premature polymerization due to the high reactivity of this product, keep it tightly sealed and store away from heat sources and direct sunlight. It is recommended to maintain storage temperature below 30 °C. Unused product should be promptly resealed and must not be left open. Under ventilated conditions at 25 °C, the product has a safe storage period of 6 months. Available packaging: 50 kg / 200 kg per drum
Tips:L-9203W is used for water-based PU topcoat, with high cost performance and good weather resistance.
Related Products
| Product | Description |
|---|---|
| L-9203W | Water-based Cost-effective PU Topcoat Resin |
| L-9211W | Water-based PU Plastic Primer Resin |
| L-9400W | PU Quick-drying Wear-resistant Resin |
| L-9500W | Water-based PU High Wear-resistant Resin |
Note: Technical data represents typical values only. In view of the differences in formulas, production process, conditions, all the above statements must be adjusted according to the actual situation, our company does not make any promises. Our company reserves the right to reform its products without prior notice of any changes.
Contact Person: Yuki
Tel: +86 18027002837(WhatsApp)
Email: service@lencolo37.com