Application ：Original car paint, motorcycle varnish, high-demand plastic paint, two-component PU varnish or solid color paint for various metals and plastics, Monocoat high-gloss black paints.
Contact UsDescription
L-1255 is an acrylic copolymer with high solid content and medium hydroxyl content. When paired with non-yellowing polyisocyanate at room temperature, it can be made into a two-liquid system with good construction performance, high fullness and excellent matching performance. It is very suitable for double The liquid type is coated with high-gloss black paint and gloss varnish. It has good adhesion to substrates such as ABS, PC, PC fiber reinforced, PMMA, fiberglass, various metals, etc.
Chemical & physical data
| Appearance | Colorless transparent liquid |
|---|---|
| Viscosity (25ºC, CPS) | 2,000 - 5,000 |
| Solid content % | 65±2 |
| OH value (solid) | 121 mgKOH/g |
| OH % (solid) | 3.6 |
| Acid value (solid) | 6 mgKOH/g |
Performance
Good fullness, good gloss, high leveling, quick drying, good adhesion and good weather resistance.
Guideline formulation
| High gloss black paint | Thinner | ||
|---|---|---|---|
| L-1255 resin | 60 | Ethyl acetate | 35 |
| T-12 (drier) | 0.1 | Butyl acetate | 45 |
| Lencolo 3160 | 0.4 | PMA | 20 |
| Lencolo 3137 | 0.2 | ||
| Lencolo 8531 | 0.3 | ||
| PU special black paste | 23 | ||
| Thinner | 16 | ||
| Curing agent N3390 60 : Butyl ester 40 | |||
| Main agent: Curing agent: Thinner =3 : 1 : (1~2) | |||
Application
Original car paint, motorcycle varnish, high-demand plastic paint, two-component PU varnish or solid color paint for various metals and plastics, Monocoat high-gloss black paints.
Storage, shelf time and Packing
To prevent the product from polymerization and gelling, please keep it sealed and away from heat and light. Recommended storage temperature is not higher than 30°C. Unused products must be sealed and stored in a timely manner and cannot be stored in the open. Safe storage time is 6 months at room temperature( 25ºC) and under ventilation. 20KG/25KG/190KG/barrel
Tips:L-1255 can be used to make a black PU coating with good leveling, good fullness and boiling resistance.
Related Products
| Product | Description |
|---|---|
| L-1200A | Good Adhesion PU Resin |
| L-1200B | Good Adhesion PU Resin for Inks |
| L-1201 | High Solid Content PU Primer Resin |
| L-1202 | PU Primer Resin for Nylon+Fiber |
| L-1250 | PU Resin for Metallic Paint |
| L-1251 | RCA Resistant PU Resin |
| L-1253 | High Solid Content PU Resin |
| L-1254 | Fast Drying High Solid Content PU Resin |
| L-1255 | Monocoat High-gloss Black PU Resin |
| L-1256 | Fast Drying High Hydroxyl PU Resin |
| L-1257 | High Weather-resistant High Fullness PU Resin |
| L-1258 | High Gloss PU Resin |
| L-1260 | PU Resin for Optical Coating |
| L-1380 | High Flexibility Polyester Resin |
Note: Technical data represents typical values only. In view of the differences in formulas, production process, conditions, all the above statements must be adjusted according to the actual situation, our company does not make any promises. Our company reserves the right to reform its products without prior notice of any changes.